环氧磷酸锌底漆IP38

Epoxy Zinc Phosphate Primer IP38

产品说明  Description
IP38为含有磷酸锌防腐蚀颜料的环氧双组份防锈底漆。用聚酰胺固化。具有漆膜坚硬、高效耐腐蚀等特点。在潮湿表面也可涂布本漆(详见备注)。 IP38 is a two-component epoxy rust-inhibiting primer containing zinc phosphate corrosion inhibiting pigment. Cured with polyamide. It features tough film, high performance anticorrosion. It can be painted on moist surface. (See remarks).
主要特性  Outstanding Characteristics
1.     钢板现场喷砂后涂布于表面作临时保护膜。 2.     用作环氧漆系列和聚氨酯漆系列的通用底漆。 3.     用于中等至严重程度腐蚀环境中的钢或其它金属表面涂布。 4.     还可用于集装箱油漆配套中的底漆和中间漆或箱内的面漆。 聚酰胺固化剂H330用于热带及亚热带气候的施工，聚酰胺加成物H350则能在低温固化。 1.  As a blastprimer for temporary protection of steel blast cleaned on site. 2.  As a general purpose, primer for epoxy and polyurethane series. 3.  As a primer or an intermediate coat in paint system for container or a top coat on its interior surface. 4.  On steel and other metal surfaces in moderately to severely corrosive environment. Curing agent H330, polyamide, is suitable for application in tropical and subtropical weather. Curing agent H350, polyamide adduct, can be cured at low temperature.
技术数据  Technical Data
漆    面: Finish :	平光  Flat
颜    色: Colors:	红色 Red	灰色 (也可根据需要提供其它颜色)。 Grey  (or other color available on request)
体积固体含量: Volume solids:	约51% Approx.51%
理论涂布率: Theoretical spreading rate:	10 m2/L    (以 50 微米干膜计) 10 m2/L    (50 micron dry film thickness )
耐    温： Temperature resistance:	(干燥): 140℃ Max. (Dry):
闪    点: Flash point:	26℃
比    重: Specific gravity:	约 1.3 kg/L Approx. 1.3 kg/L
指 触 干: Dry to touch:	3-4 小时        20℃ Approx. 3-4 hours
完全固化: Fully cured:	7 天 7 days
施工详述  Application Details
固  化 剂: Curing agent:	H330 或 H350 H330 or H350
混合比例: Mixing ratio:	基料 IP38 ：固化剂=  4 : 1 Base IP38 :  Curing agent  = 4 : 1			(体积比) ( by volume
施工方法: Application method:	无空气喷涂 Airless spray	空气喷涂 Air spray					刷涂 Brush (touch-up)
稀 释  剂: Thinner:	TH90	TH90					TH90
用量: Max. Vol.:	5%	15%					5%
混合使用时间: Pot life:	8 小时    (20℃,H330) 8 hours	4小时    (20℃，H350) 4 hours
漆膜厚度: Indicated film thickness:	湿膜:  100 微米 Wet:   100 micron	干膜: 50 微米    (见“备注”) Dry: 50 micron    (see Remarks)
重涂间隔: Recoat interval:	最小: 6小时  (20℃) Min.:  6 hours	: 30天   (20℃)   (见“备注”) Max.: 30 days          (See remarks)
表面处理: Surface preparation:	新钢材：喷砂清洁至Sa2.5级标准。若需要，可喷涂适当的车间底漆临时保护钢板表面。涂漆之前，应将贮运与加工期间受损的车间底漆和受污染部位清洗干净，再用本品修补。其它金属，如电镀钢板和轻合金板应彻底清洗油脂，喷砂去除污染物以确保附着力。 维修：用适当的清洁剂清除所有油迹、滑脂等。用高压淡水清洗掉盐迹和其它污染物。用干(或湿)喷砂或动力工具清除所有锈迹和松散漆膜。磨刮边角使其平整。湿喷后应用淡水冲净表面，待表面达到微湿或潮湿状态时（见“备注”)，修补破损部位至原漆膜厚度。 大型修补/新钢材(潮湿条件下)应干(或湿)喷砂至Sa2.5级标准。若是湿喷，可用适当的缓蚀剂。最后涂覆之前，必须用高压淡水清洗掉多余的缓蚀剂和残砂。（注意：缓蚀剂一般不适用于即将浸泡的表面） New steel: Abrasive blasting to Sa2.5. For temporary protection, if required, use suitable shopprimer. All damage of shopprimer and contamination from storage and fabrication should be thoroughly cleaned prior to final painting. For repair and touch-up use Lanpoker’s epoxy zinc phosphate primer IP38.On other metals (e.g. electroplated steel plate and light alloys): Thoroughly degreasing and light abrasive sweeping to remove all contaminants and to secure adhesion. Maintenance: Remove oil and grease, etc. with suitable cleaner. Remove salt and other contaminants by high pressure fresh water cleaning. Remove all rust and loose material by dry (or wet) abrasive blasting or power tool cleaning. Feather edges to sound and intact areas. After wet blasting, clean the surface with fresh water. Touch up to full film thickness after moist or damp surfaces appear. (see Remarks).  Large scale repairing/new steel(under damp condition): Dry (or wet) blasting to Sa2.5. If wet blasting is used, suitable corrosion inhibitor can be used. High-pressure fresh water should be applied to remove residues before the final coating. (Attention: Corrosion inhibitor is generally not suitable for the surface which is to be soaked.)
施工条件: Application conditions:	仅在温度-10℃(固化剂H350)和10℃(固化剂H330)以上条件下使用本品，才能使施工和固化得以正常进行。在冰点及冰点以下温度条件下，施工前应确认表面无结冰现象，否则会影响漆膜附着力。油漆本身的温度应高于15℃，以获得良好的施工效果。 Use curing agent H330 only when application and curing can proceed at temperature above 10℃. While use curing agent H350 the surface temperature should also be above -10℃. As temperature at / below freezing point, freezing may occur on the surface and influence the adhesion of the film , therefore the temperature of the paint should be above 15℃ to ensure normal application performance.
加涂油漆: Subsequent coat:	环氧厚浆漆IH35、或按规定加涂 Epoxy hi-build paint IH35, or according to specification.
备注  Remarks
漆膜厚度: Indicated film thickness:	可根据使用目的和区域修改漆膜厚度，但这会相应地改变涂布率、稀释量、干燥时间和重涂间隔。干膜的正常范围为：25-100微米。若作喷砂底漆，则应避免漆膜过厚。漆膜厚度应为40微米左右。想达到这一效果，需要额外稀释。
	May be specified in another film thickness than indicated depending on purpose and area of use. This will alter spreading rate, thinning amount, and drying time and recoat interval. Normal range for dry film is 25-100 micron. If used as ablast primer, excessive film thickness must be avoided. Optimum dry film thickness for this purpose is approximately 40 micron. To achieve this, additional thinning may be necessary.
重涂间隔: Recoat interval:	对内部表面，IP38没有重涂间隔。 No maximum recoat interval on interior surfaces. 在温度20℃时，采用下列品种复涂时的重涂间隔为： Maximum recoat intervals at 20℃, overcoated with:
	氯化橡胶厚浆漆 Hi-build chlorinated rubber Paint				24小时  24hours
	聚氨酯漆系列 Polyurethane series				3天 3days
	环氧漆系列 Epoxy series				30天  30days
	外表面的重涂间隔仅适用于漆膜在使用期间受周期性浸渍、重露、大温差、化学品侵蚀和磨损的情况。在其它情况下对于环氧漆来说无重涂间隔。暴露于污染环境下，重涂之前，应用 (高压)淡水彻底清洗表面，任其自干。如果超过重涂间隔，必须磨粗表面以确保涂层间的附着力。 Maximum recoat interval refers to surfaces exposed to periodical immersion, heavy condensation, great variations in temperature, chemical attack, and/or abrasion during service life of the coating system. Under other service conditions no maximum recoat interval for epoxies. Before overcoating after exposure in contaminated environment, clean the surface thoroughly by high pressure fresh water hosing and allow to drying. If maximum recoat interval is exceeded, roughening of the surface is necessary to ensure intercoat adhesion.
安全  Precautions
本产品在施工时应遵守有关的国家卫生，安全和环境标准及其法规。使用前应获取和咨询有关本产品的材料安全数据表。注意包装标签上的安全事项。如果你没有完全理解或你不能严格执行这些安全事项，不要使用本产品。 在施工和干燥期间要采取通风措施，维持溶剂蒸汽的容度在安全极限内，防止中毒或缺氧。小心避免与皮肤、眼睛接触。 All work involving the application and use of this product should be performed in compliance with all relevant national Health, Safety and Environmental standards and regulations. Prior to use, obtain, consult and follow the Material Safety Data Sheet for this product concerning health safety information. Read and follow all precautionary notices on the Material Safety Data Sheet container labels. If you do not fully understand these warnings and instructions or if you cannot strictly comply with them, do not use this product. Proper ventilation measures must be provided during application and drying to keep solvent vapor concentrations within safe limits and to protect against toxic or oxygen deficient hazards. Take precautions to avoid skin and eye contact (i.e. Gloves, goggles, face masks, barrier creams etc.) Actual safety measures are dependant on application methods and work environment.
附注  Other Notice
本说明书有关数据是在标准条件下取得，实际使用时，环境条件可能与之略有不同，以上数据如有改变，以本公司说明书为准，恕不另行通知。 All information in this product data sheet is based on standard conditions and slight variation may occur with different conditions. All information in our company is subject to change without notice.