   平川（国际）塑胶贸易有限公司长期供应-BASF AG‘德国巴斯夫公司’Ultraform POM：Ultraform N 2640 Z6 UNC     Acetal (POM) Copolymer

Ultraform N 2640 Z6 UNC POM BASF 冲击改性的POM：

Ultraform N 2640 Z2 UNC Q600   Acetal (POM) Copolymer

Ultraform N 2640 Z4 BK140 Q600   Acetal (POM) Copolymer

Ultraform N 2640 Z4 UNC Q600   Acetal (POM) Copolymer

Ultraform N 2640 Z6 UNC   Acetal (POM) Copolymer

Ultraform N 2640 Z6 UNC POM BASF特点：

  特点：Ultraform N 2640 Z6 UNC，本色，弹性体冲击改性的共聚甲醛，具有高抗冲击性的特点，适用于汽车外部零件，玩具和紧固件；注塑成型。

Ultraform N 2640 Z6 UNC POM BASF

Physical Properties	Metric	English	Comments
Density	1.33 g/cc	0.0480 lb/in3	ISO 1183
Water Absorption	1.10 %	1.10 %	ISO 62
Moisture Absorption at Equilibrium	0.250 %	0.250 %	23°C/50% R.H.; ISO 62
Linear Mold Shrinkage	0.0190 cm/cm	0.0190 in/in	ASTM Data; MD
Linear Mold Shrinkage, Flow	0.0160 cm/cm	0.0160 in/in	ISO Data
Linear Mold Shrinkage, Transverse	0.0160 cm/cm	0.0160 in/in	ISO Data
Melt Flow	4.50 g/10 min @Load 2.16 kg, Temperature 190 °C	4.50 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	37.0 MPa	5370 psi	50mm/min; ISO 527
	37.0 MPa	5370 psi	2 in/min; ASTM Test
Elongation at Break	>= 50.0 %	>= 50.0 %	50mm/min, Nominal strain; ISO 527
Elongation at Yield	17.0 %	17.0 %	50mm/min; ISO 527
	17.0 %	17.0 %	2 in/min; ASTM Test
Tensile Modulus	1.30 GPa	189 ksi	1mm/min; ISO 527
	1.36 GPa	197 ksi	ASTM Test
Flexural Modulus	1.32 GPa	191 ksi	ASTM Test
Charpy Impact Unnotched	NB	NB	ISO 179
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	ISO 179
Charpy Impact, Notched	1.80 J/cm2	8.57 ft-lb/in2	ISO 179
	0.900 J/cm2 @Temperature -30.0 °C	4.28 ft-lb/in2 @Temperature -22.0 °F	ISO 179
Tensile Creep Modulus, 1 hour	825 MPa	120000 psi	ISO 899
Tensile Creep Modulus, 1000 hours	575 MPa	83400 psi	ISO 899
Izod Impact, Notched	0.590 J/cm @Temperature -40.0 °C	1.11 ft-lb/in @Temperature -40.0 °F	ASTM Test
	1.55 J/cm @Thickness 3.17 mm	2.90 ft-lb/in @Thickness 0.125 in	ASTM Test

Ultraform N 2640 Z6 UNC POM BASF

力学性能　　

POM强度、刚度高，弹性好，减磨耐磨性好。其力学性能优异，比强度可达50.5MPa，比刚度可达2650MPa，与金属十分接近。POM的力学性能随温度变化小，共聚POM比均聚POM的变化稍大一点。POM的冲击强度较高，但常规冲击不及ABS和PC；POM对缺口敏感，有缺口可使冲击强度下降90%之多。POM的疲劳强度十分突出，10交变载荷作用后，疲劳强度可达35PMa，而PA和PC仅为28MPa。POM的蠕变性与PA相似，在20℃、21MPa、3000h时仅为2.3%，而且受温度的影响很小。POM的摩擦因数小，耐磨性好（POM>PA66>PA6>ABS>HPVC>PS>PC），极限PV值很大，自润滑性好。POM制品对磨时，高载荷作用时易产生类似尖叫的噪声。