Physical Properties	Metric	English	Comments
Density	1.42 g/cc	0.0513 lb/in3	ISO 1183
Water Absorption	0.600 % @Temperature 23.0 °C	0.600 % @Temperature 73.4 °F	Immersion 24h; ISO 62, Similar to
Moisture Absorption at Equilibrium	0.300 % @Temperature 23.0 °C	0.300 % @Temperature 73.4 °F	Equilibrium 50%RH; ISO 62, Similar to
Water Absorption at Saturation	1.40 % @Temperature 23.0 °C	1.40 % @Temperature 73.4 °F	Saturation, immersed; ISO 62, Similar to
Linear Mold Shrinkage, Flow	0.0200 cm/cm @Thickness 2.00 mm	0.0200 in/in @Thickness 0.0787 in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.0190 cm/cm @Thickness 2.00 mm	0.0190 in/in @Thickness 0.0787 in	ISO 294-4
Melt Flow	7.00 g/10 min @Load 2.16 kg, Temperature 190 °C	7.00 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	70.0 MPa @Temperature 23.0 °C	10200 psi @Temperature 73.4 °F	ISO 527
Elongation at Break	35.0 % @Temperature 23.0 °C	35.0 % @Temperature 73.4 °F	ISO 527
Elongation at Yield	18.0 % @Temperature 23.0 °C	18.0 % @Temperature 73.4 °F	ISO 527
Tensile Modulus	3.00 GPa @Temperature 23.0 °C	435 ksi @Temperature 73.4 °F	ISO 527
Flexural Modulus	2.90 GPa @Temperature 23.0 °C	421 ksi @Temperature 73.4 °F	ISO 178
Charpy Impact, Notched	0.800 J/cm2 @Temperature -30.0 °C	3.81 ft-lb/in2 @Temperature -22.0 °F	ISO 179/1eA
	1.10 J/cm2 @Temperature 23.0 °C	5.23 ft-lb/in2 @Temperature 73.4 °F	ISO 179/1eA
Tensile Creep Modulus, 1 hour	2700 MPa @Temperature 23.0 °C	392000 psi @Temperature 73.4 °F	ISO 899
Tensile Creep Modulus, 1000 hours	1500 MPa @Temperature 23.0 °C	218000 psi @Temperature 73.4 °F	ISO 899