Physical Properties |
Metric |
English |
Comments |
Density |
1.42 g/cc |
0.0513 lb/in3 |
Water Absorption |
0.390 % @Temperature 23.0 °C |
0.390 % @Temperature 73.4 °F |
Linear Mold Shrinkage, Flow |
0.0180 cm/cm @Thickness 2.00 mm |
0.0180 in/in @Thickness 0.0787 in |
Linear Mold Shrinkage, Transverse |
0.0200 cm/cm @Thickness 2.00 mm |
0.0200 in/in @Thickness 0.0787 in |
Melt Flow |
1.90 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.90 g/10 min @Load 4.76 lb, Temperature 374 °F |
|
2.40 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.40 g/10 min @Load 4.76 lb, Temperature 374 °F |
|
Mechanical Properties |
Metric |
English |
Comments |
Tensile Strength, Yield |
72.0 MPa @Temperature 23.0 °C |
10400 psi @Temperature 73.4 °F |
Elongation at Break |
40.0 % @Temperature 23.0 °C |
40.0 % @Temperature 73.4 °F |
Elongation at Yield |
22.0 % @Temperature 23.0 °C |
22.0 % @Temperature 73.4 °F |
Tensile Modulus |
3.10 GPa @Temperature 23.0 °C |
450 ksi @Temperature 73.4 °F |
Flexural Modulus |
2.90 GPa @Temperature 23.0 °C |
421 ksi @Temperature 73.4 °F |
Charpy Impact, Notched |
0.900 J/cm2 @Temperature -30.0 °C |
4.28 ft-lb/in2 @Temperature -22.0 °F |
|
1.20 J/cm2 @Temperature 23.0 °C |
5.71 ft-lb/in2 @Temperature 73.4 °F |
Izod Impact, Notched (ISO) |
10.0 kJ/m2 @Temperature 23.0 °C |
4.76 ft-lb/in2 @Temperature 73.4 °F |