POM Ultraform N 2320 U017 UNC Q600 BASF物性表：

Physical Properties	Metric	English	Comments
Density	1.41 g/cc	0.0509 lb/in3	ISO 1183
Linear Mold Shrinkage	0.0200 cm/cm	0.0200 in/in	ASTM Data; MD
Melt Flow	9.00 g/10 min @Load 2.16 kg, Temperature 190 °C	9.00 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	61.0 MPa	8850 psi	50mm/min; ISO 527
	61.0 MPa	8850 psi	2 in/min; ASTM Test
Elongation at Break	>= 50.0 %	>= 50.0 %	50mm/min, Nominal strain; ISO 527
Elongation at Yield	11.0 %	11.0 %	50mm/min; ISO 527
	11.0 %	11.0 %	2 in/min; ASTM Test
Tensile Modulus	2.60 GPa	377 ksi	1mm/min; ISO 527
Charpy Impact, Notched	0.600 J/cm2	2.86 ft-lb/in2	ISO 179
	0.600 J/cm2 @Temperature -30.0 °C	2.86 ft-lb/in2 @Temperature -22.0 °F	ISO 179
Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	150 °C	302 °F	ISO 75
Deflection Temperature at 1.8 MPa (264 psi)	90.0 °C	194 °F	ISO 75

    POM Ultraform N 2320 U017 UNC Q600 BASF

成形性　　

结晶料,熔融范围窄，熔融和凝固快，料温稍低于熔融温度即发生结晶。流动性中等。吸湿小，可不经干燥处理。