POM Hostaform S9063 TICONA

    平川（国际）塑胶贸易有限公司长期现货供应-‘Ticona’美国泰科纳公司Hostaform POM 共聚甲醛-Hostaform POM：POM Hostaform S9063 TICONA

POM Hostaform S9063 TICONA 泰科纳POM 特点：

    TICONA POM HOSTAFORM S9063，冲击改性共聚甲醛，注塑型，具有较高的冲击强度，硬度略低，具有高耐热和抗氧化的特性，用于模塑部件，UL94检测，1.5MM/HB。

POM Hostaform S9063 TICONA 泰科纳POM 应用：

    3．聚甲醛还可以用于耐腐蚀的消防水龙头，钢笔的笔杆和笔套、玩具、梳子、拉链、睫毛油棒等消费品等等。POM Hostaform S9063 TICONA 泰科纳POM 物性表：

Physical Properties	Metric	English	Comments
Density	1.39 g/cc	0.0502 lb/in3	10x10x4 mm from multi-purpose test specimen (ISO 3167); ISO 1183
Water Absorption	0.200 %	0.200 %	80x80x1mm, at 23°C and 50% RH; ISO 62
Water Absorption at Saturation	0.650 %	0.650 %	80x80x1mm, 23°C; ISO 62
Melt Flow	11.12 g/10 min @Load 2.16 kg, Temperature 190 °C	11.12 g/10 min @Load 4.76 lb, Temperature 374 °F	Calculated from Volume flow Rate: 8 cm3/10min; ISO 1133
Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	110 MPa	16000 psi	30 sec value, 20x20x4 mm; ISO 2039, part 1; applied load 358 N
Tensile Strength, Yield	53.0 MPa	7690 psi	multi-purpose test specimen (ISO 3167); ISO 527, part 1/2; test speed 50 mm/min
Elongation at Break	32.0 %	32.0 %	multi-purpose test specimen (ISO 3167); ISO 527, part 1/2; test speed 50 mm/min
Elongation at Yield	9.00 %	9.00 %	multi-purpose test specimen (ISO 3167); ISO 527, part 1/2; test speed 50 mm/min
Tensile Modulus	2.10 GPa	305 ksi	multi-purpose test specimen (ISO 3167); ISO 527, part 1/2; test speed 1 mm/min
Flexural Modulus	2.00 GPa	290 ksi	80x10x4mm from multi-purpose test specimen (ISO 3167); ISO 178
Charpy Impact Unnotched	22.0 J/cm2 @Temperature -30.0 °C	105 ft-lb/in2 @Temperature -22.0 °F	80x10x4 m from multi-purpose test specimen (ISO 3167); ISO 179 1eU
	25.0 J/cm2 @Thickness 4.00 mm, Temperature 23.0 °C	119 ft-lb/in2 @Thickness 0.157 in, Temperature 73.4 °F	80x10x4 m from multi-purpose test specimen (ISO 3167); ISO 179 1eU
Charpy Impact, Notched	0.700 J/cm2 @Temperature -30.0 °C	3.33 ft-lb/in2 @Temperature -22.0 °F	80x10x4 m from multi-purpose test specimen (ISO 3167); ISO 179 1eA
	1.20 J/cm2 @Thickness 4.00 mm, Temperature 23.0 °C	5.71 ft-lb/in2 @Thickness 0.157 in, Temperature 73.4 °F	80x10x4 m from multi-purpose test specimen (ISO 3167); ISO 179 1eA
Penetration	8.00	8.00	mm, deformation damage, 60x60x3mm; ISO 6603, part 2
	20.0	20.0	J, work to damage, 60x60x3 mm; ISO 6603, part 2
Tensile Creep Modulus, 1 hour	1800 MPa	261000 psi	multi-purpose test specimen (ISO 3167); ISO 899, part 1
Tensile Creep Modulus, 1000 hours	1000 MPa	145000 psi	multi-purpose test specimen (ISO 3167); ISO 899, part 1