| Physical Properties |
Metric |
English |
Comments |
| Density |
1.43 g/cc |
0.0517 lb/in3 |
| Linear Mold Shrinkage, Flow |
0.0180 cm/cm
@Thickness 2.00 mm |
0.0180 in/in
@Thickness 0.0787 in |
| |
0.0190 cm/cm
@Thickness 4.00 mm |
0.0190 in/in
@Thickness 0.157 in |
| Linear Mold Shrinkage, Transverse |
0.0170 cm/cm
@Thickness 2.00 mm |
0.0170 in/in
@Thickness 0.0787 in |
| Melt Flow |
2.20 g/10 min
@Load 2.16 kg,
Temperature 190 °C |
2.20 g/10 min
@Load 4.76 lb,
Temperature 374 °F |
| |
| Mechanical Properties |
Metric |
English |
Comments |
| Tensile Strength, Yield |
71.0 MPa
@Temperature 23.0 °C |
10300 psi
@Temperature 73.4 °F |
| Elongation at Break |
33.0 %
@Temperature 23.0 °C |
33.0 %
@Temperature 73.4 °F |
| Elongation at Yield |
25.0 %
@Temperature 23.0 °C |
25.0 %
@Temperature 73.4 °F |
| Tensile Modulus |
3.00 GPa
@Temperature 23.0 °C |
435 ksi
@Temperature 73.4 °F |
| Flexural Modulus |
2.80 GPa
@Temperature 23.0 °C |
406 ksi
@Temperature 73.4 °F |
| Charpy Impact Unnotched |
15.0 J/cm2
@Temperature 23.0 °C |
71.4 ft-lb/in2
@Temperature 73.4 °F |
| Charpy Impact, Notched |
0.800 J/cm2
@Temperature -30.0 °C |
3.81 ft-lb/in2
@Temperature -22.0 °F |
| |
0.900 J/cm2
@Temperature 23.0 °C |
4.28 ft-lb/in2
@Temperature 73.4 °F |