Physical Properties |
Metric |
English |
Comments |
Density |
1.40 g/cc |
0.0506 lb/in3 |
Linear Mold Shrinkage, Flow |
0.0200 cm/cm @Thickness 2.00 mm |
0.0200 in/in @Thickness 0.0787 in |
Linear Mold Shrinkage, Transverse |
0.0180 cm/cm @Thickness 2.00 mm |
0.0180 in/in @Thickness 0.0787 in |
Melt Flow |
1.70 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.70 g/10 min @Load 4.76 lb, Temperature 374 °F |
|
2.50 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.50 g/10 min @Load 4.76 lb, Temperature 374 °F |
|
Mechanical Properties |
Metric |
English |
Comments |
Tensile Strength, Yield |
70.0 MPa @Temperature 23.0 °C |
10200 psi @Temperature 73.4 °F |
Elongation at Break |
45.0 % @Temperature 23.0 °C |
45.0 % @Temperature 73.4 °F |
|
65.0 % @Temperature 23.0 °C |
65.0 % @Temperature 73.4 °F |
Elongation at Yield |
18.0 % @Temperature 23.0 °C |
18.0 % @Temperature 73.4 °F |
Tensile Modulus |
3.00 GPa @Temperature 23.0 °C |
435 ksi @Temperature 73.4 °F |
Flexural Modulus |
2.80 GPa @Temperature 23.0 °C |
406 ksi @Temperature 73.4 °F |
Charpy Impact Unnotched |
17.0 J/cm2 @Temperature -30.0 °C |
80.9 ft-lb/in2 @Temperature -22.0 °F |
|
25.0 J/cm2 @Temperature 23.0 °C |
119 ft-lb/in2 @Temperature 73.4 °F |
Charpy Impact, Notched |
0.700 J/cm2 @Temperature -30.0 °C |
3.33 ft-lb/in2 @Temperature -22.0 °F |
|
0.900 J/cm2 @Temperature 23.0 °C |
4.28 ft-lb/in2 @Temperature 73.4 °F |
Izod Impact, Notched (ISO) |
8.00 kJ/m2 @Temperature 23.0 °C |
3.81 ft-lb/in2 @Temperature 73.4 °F |