Material Notes:

Delrin? 100 is a high viscosity acetal homopolymer for use in easy to fill molds. Delrin? 100 provides maximum toughness in the product line without modification, and optimum mechanical performance

Physical Properties	Metric	English	Comments
Specific Gravity	1.42 g/cc	1.42 g/cc	ASTM D 792
Density	1.42 g/cc	0.0513 lb/in3	ISO 1183
Water Absorption	0.270 % @Temperature 23.0 °C	0.270 % @Temperature 73.4 °F	Immersion 24h; ASTM D 570
Moisture Absorption at Equilibrium	0.200 % @Temperature 23.0 °C	0.200 % @Temperature 73.4 °F	Equilibrium 50%RH; ISO 62, Similar to
	0.220 % @Temperature 23.0 °C	0.220 % @Temperature 73.4 °F	Equilibrium 50%RH; ASTM D 570
Water Absorption at Saturation	0.900 % @Temperature 23.0 °C	0.900 % @Temperature 73.4 °F	Saturation; ASTM D 570
	0.900 % @Temperature 23.0 °C	0.900 % @Temperature 73.4 °F	Saturation, immersed; ISO 62, Similar to
Linear Mold Shrinkage, Flow	0.0200 cm/cm @Thickness 2.00 mm	0.0200 in/in @Thickness 0.0787 in	ISO 294-4
	0.0210 cm/cm @Thickness 2.00 mm	0.0210 in/in @Thickness 0.0787 in	ISO 294-4
	0.0180 - 0.0210 cm/cm @Thickness 3.20 mm, Time 24.0 hour	0.0180 - 0.0210 in/in @Thickness 0.126 in, Time 24.0 hour	ASTM D 955
Linear Mold Shrinkage, Transverse	0.0140 cm/cm @Thickness 2.00 mm	0.0140 in/in @Thickness 0.0787 in	ISO 294-4
	0.0190 cm/cm @Thickness 2.00 mm	0.0190 in/in @Thickness 0.0787 in	ISO 294-4
	0.0180 - 0.0210 cm/cm @Thickness 3.20 mm, Time 24.0 hour	0.0180 - 0.0210 in/in @Thickness 0.126 in, Time 24.0 hour	ASTM D 955
Melt Flow	1.00 g/10 min @Load 1.05 kg, Temperature 190 °C	1.00 g/10 min @Load 2.31 lb, Temperature 374 °F	ASTM D 1238
	1.90 g/10 min @Load 2.16 kg, Temperature 190 °C	1.90 g/10 min @Load 4.76 lb, Temperature 374 °F	[cm3/10 min]; ISO 1133
	2.30 g/10 min @Load 2.16 kg, Temperature 190 °C	2.30 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133